| Epoxy/PVC |
| ←Back |
|
|
Require a high standard of cleanliness, landscaping, dust-free, sterile and static defense electronics, microelectronics, telecommunications, computer manufacturing industry and sophisticated equipment of large-scale plants.
■ Performance characteristics
 1.；Excellent antistatic effects lasting from time, can not be affect by temperature and humidity; 2.Use solvent-free epoxy curing agent produced increases quality; 3.Smooth surface, landscaping, reached mirror effects; 4.Acid, alkali, salt, oil and other media corrosion resistant alkali particularly good;5.Wear-resistant, pressure, impact resistance, a certain amount of flexibility. Acid, alkali, salt, oil and other media corrosion resistant alkali particularly good
■Life :1mm thickness of more than eight years of life.
■ Construction Technology 1.Base; 2.Brushing closed primer; 3.By painting the middle section；
4.Polishing, cleaning;5.Anti-static self-leveling Epoxy Paint trowel 1-2 times. |
|
|
|
| project |
indicators |
| Drying time |
surface dry |
≤6 |
| Solid dry |
≤24 |
| Tensile Strength ,Mpa |
≤9 |
| Flexural strength,Mpa |
≥7 |
| Arrived compressive strength ,Mpa |
≥85 |
| shao shi hardness |
≥70 |
| LEVELING ,cm |
≥5min |
| Wear resistance (750g/500r, weightlessness g) |
≤0.02 |
| 60% of sulfate-resistant |
minor change to allow 30 days |
| 25% sodium hydroxide |
30 days without unusual resistance |
| 3% drip-resistant abnormal |
30 days without unusual resistance |
| Gas oil-resistant, resistant 120# |
Be able to bear |
| Adhesive Strength ,Mpa |
≥2 |
| Surface Resistivity ,Ω |
106～109 |
| Volume Resistivity ,Ω |
106～109 |
|
 |
|
|
|
 |
|
| Epoxy/PVC |
|
|
 |
|